SPESIFICATION

Over View

Glass Reinforced Concrete (GRC) is a composite material consisting of a mortar of hydraulic cement and fine aggregate reinforced with alkali resistant glass The GRC may contain additional filler materials, pozzolanic materials and admixtures. The fiber contents are typically 3% to 5% by weight depending on product application and production method employed. The properties of GRC depend on a wide range of variables. These include method of manufacture, mix formulation, fiber product type, length and orientation, admixtures used, etc. The information given is mainly refers to GRC made by the spray and premix processes. These GRC materials have been widely used for many years and their properties and characteristics studied extensively.

Ikhtisar

GRC adalah bahan komposit yang terdiri dari campuran semen dan pasir, diperkuat dengan fiber yang tahan terhadap alkali . GRC kadang juga dicampur tambahan material pengisi dan campuran lainnya . Kandungan fiber umumnya berkisar antara 3% sampai 5% dari berat tergantung dari peggunaan metode produksinya. Sifat pada GRC sangat berfariasi tergantung dari metode pembuatan , rumus campuran , tipe dari fiber , panjang fiber , dan bahan campuran yang dipakai. Informasi yang diberikan dibawah ini adalah untuk GRC yang dibuat dengan proses penyemprotan dan proses premix. Material GRC telah digunakan secara luas selama bertahun-tahun dan sifat-sifat serta karakternya dipelajari secara sekstensif.

Raw Material

Glassfiber reiforced concrete are mainly used in exterior building façade panels and as architectural precast concrete. Glass fiber reinforced concrete consists of high strength glass fiber embedded in a cementitious matrix.

Bahan Dasar

GRC umumnya digunakan untuk panel dinding eksterior bangunan dan sebagai bahan arsitektural pracetak . GRC terdiri dari glass fiber berkekuatan tinggi yang tertanam dalam ikatan semen.

Alkali-Resistant Glass Fiber

Glass fiber shall be an alkali-resistant, continuous filament fiber developed and formulated minimum

The glass fiber must have a minimum ZrO2 content of 16% by weight , in accordance with internationally reqognized standards,and must have a minimum strenght retention of 300 Mpa.

Suitable alkali resistant glass fibres are Cem-Fil manufactured by SINOMA Taishan Fiberglass Inc , NEG ARG Fiber manufactured by Nippon Electric Glass or equal approved.

Alkali-resistant Fiber Glass

Fiber glass harus digunakan alkali resistant , serat memanjang yang dikembangkan dengan formula khusus yang menjadikannya kekuatan tinggi tahan terhadap lingkungan semen.

Fiber glass ini harus memiliki kandungan ZrO2 minimum 16% dari berat , sesuai standar internasional dan harus mempunyai kekuatan tarik minimum 300Mpa.

Fiber glass yang sesuai untuk keperluan ini adalah Cem-Fil yang diproduksi oleh SINOMA Taishan Fiberglass Inc , NEG ARG Fiber yang diproduksi oleh Nippon Electric Glass atau yang setara dan disetujui.

Portland Cement

The cement shall be Ordinary Portland Cement supported by suitable certification ( Cement Type I ) . Cement shall be obtained from one source throughout process of production. Cement shall be correctly stored and kept dry to avoid deterioration

Semen

Semen yang seharusnya adalah Portland Cement yang telah memiliki sertifikasi ( semen tipe-1 ) .Semen harus diambil dari sumber yang sama dalam satu proses produksi dan disimpan terjaga dalam keadaan kering untuk menghindari kemerosotan mutu.

Sand

Sand should be washed and dried to remove soluble matter, and to permit control of the water/cement ratio. Sand added to the mix shall not exceed 50% by weight of the total mix and sand/cement ratio shall not exceed.

Pasir

Pasir harus pasir telah dicuci dan kering , bersih dari kotoran , dan sesuai terkontrol dengan perbandingan air/semen ( water cement ratio ) . Pasir dalam adukan tidak boleh melebihi 50% dari berat campuran semen pasir.

Potable Water

Water shall be potable clean and free from deleterious matter that may interfere with the color, setting, or strength of the concrete.

Air Bersih

Air adalah harus air bersih yang dapat diminum dan bersih dari kotoran yang tidak mempengaruhi warna , setingan atau kekuatan GRC .

Admixtures

None.

Bahan Campuran

Tidak digunakan.